VARIATION OF COMPOSITIONAL CONTENT IN SUBSURFACE LAYERS OF HASTELLOY TYPE ALLOYS AS CAUSED BY MELT OF FLUORIDES ZrF4 – NaF AND ELECTRON IRRADIATIONV.М. Azhazha, А.S. Bakai, Yu.P. Bobrov, А.N. Dovbnya, S.D. Lavrinenko, M.M. Pylypenko National Science Center “Kharkov Institute of Physics and Technology”, 1 Akademicheskaya Str., 61108 Kharkov, Ukraine; E-mail: azhazha@kipt.kharkov.ua The secondary-ion mass-spectrometry technique was employed to study the compositional content variation in subsurface layers of alloys of Hastelloy type that had been irradiated with electron beam with the average energy 9.6 MeV in the melt of sodium and zirconium fluoride salts at the temperature 650°С for 700 hours. | |
ИЗМЕНЕНИЕ КОМПОЗИЦИОННОГО СОСТАВА В ПРИПОВЕРХНОСТНЫХ СЛОЯХ СПЛАВОВ ТИПА ХАСТЕЛЛОЙ Н ПОД ДЕЙСТВИЕМ РАСПЛАВА ФТОРИДОВ ZrF4 – NaF И ЭЛЕКТРОННОГО ОБЛУЧЕНИЯВ.М. Ажажа, А.С. Бакай, Ю.П. Бобров, А.Н. Довбня, С.Д. Лавриненко, Н.Н. Пилипенко Методом вторично-ионной масс-спектрометрии исследовано изменение композиционного состава в приповерхност-ных слоях образцах сплавов типа Хастеллой, облученных пучком электронов со средней энергией 9,6 МэВ в расплаве солей фторидов натрия и циркония при температуре 650°С в течение 700 ч. | |
ЗМІНА КОМПОЗИЦІЙНОГО СКЛАДУ В ПОВЕРХНЕВИХ ШАРАХ СПЛАВІВ ТИПУ ХАСТЕЛОЙ Н ПІД ДІЄЮ РОЗПЛАВУ ФТОРИДІВ ZrF4 – NaF І ЕЛЕКТРОННОГО ОПРОМІНЕННЯВ.М. Ажажа, О.С. Бакай, Ю.П. Бобров, А.М. Довбня, С.Д. Лавриненко, М.М. Пилипенко Методом вторинно-іонної мас-спектрометрії досліджено зміну композиційного складу в приповерхневих шарах зра-зків сплавів типу Хастелой, опромінених пучком електронів з середньою енергією 9,6 МеВ в розплаві солей фторидів натрію і цирконію при температурі 650°С протягом 700 г. | |